Rolling technology of A387 grade 22 class 2 pressure vessel steel sheet

The company has superior geographical location and convenient transportation. After more than 20 years of market trials and tribulations, from small to large, from weak to strong, in order to meet the needs of customer extension development, the company expanded the deep A387 grade 22 class 2 pressure vessel steel sheet processing services of cutting steel pieces. Now we have built a business system integrating steel plate, steel plate cutting and A387 grade 22 class 2 pressure vessel steel sheet steel deep processing. The company provides one-stop solution for customers with lower price, higher quality and faster response speed.

Compared with 15Cr steel, 20Cr alloy has higher strength and hardenability. The critical hardening diameter in oil is 4-22mm, and the critical hardening diameter in water is 11-40mm, but the toughness is poor. This A387 grade 22 class 2 pressure vessel steel sheet alloy steel A387 grade 22 class 2 pressure vessel steel sheet still has a tendency to grow grains during carburization, and direct quenching at lower temperature has a greater impact on impact toughness, so secondary quenching is required after carburization to improve the toughness of the core of the part, and there is no temper brittleness.

A514 gr.E quenched and tempered alloy steel chemical composition (melting analysis)%
C: 0.12-0.20, Si: 0.20-0.40, Mn: 0.40-0.70, P max.: 0.035, S max.: 0.035, Cr: 1.40-2.00, Mo: 0.40-0.60, Ti: 0.01-0.10, Cu: 0.15-0.50, B: 0.001-0.005
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

We have a professional after-sales service team, the company has developed a clear service process and service standards, after-sales service team members strictly perform after-sales procedures, comply with service standards. The most important thing is that we have set up the correct concept of after-sales service, "customer first, sincere service for users".