Process specification for S355MC automobile steel plate in production

The hot rolling method is to heat the S355MC automobile steel plate steel material to about 1000 ℃ ~ 1250 ℃ and use the rolling mill to roll it. The traditional hot rolling process is generally divided into the following two steps: the first step is to use the primary rolling mill or billet rolling mill to roll the ingot, billet or continuous casting billet into a certain shape and size of billet. This kind of S355MC automobile steel plate rolling process is usually called semi-finished product production, also called blank production.

Heavy plate S355MC automobile steel plate spot in Shanghai warehouse
65*2250*4600, 110*2600*10600, 100*2600*10300, 130*2600*9350, 100*2600*11830, 140*2600*8550, 70*3020*8100, 58*2600*3300, 120*2600*9800, 100*2600*11700, 120*2600*9800, 68*2065*4500, 130*2500*9000, 180*2600*6800, 180*2600*6750, 92*3020*9600, 150*2500*7500, 100*2600*11800, 180*2600*6780, 200*2600*6130, 200*2600*5980, 200*2600*6000, 200*2600*6150.

Recently, the epidemic situation in developed countries such as Europe and the United States has become more and more serious, leading to the stagnation of economic activities in some countries, which has also affected domestic and foreign trade orders. In particular, industries such as steel, which have a long industrial chain and a wide range of industries, are more seriously affected. The development of foreign epidemic situation has different influence on the direct and indirect export of S355MC automobile steel plate and so on steel products.

S355MC automobile steel plate, Hot rolled seamless tube is usually produced on automatic tube rolling mill. After the solid tube blank is inspected and the surface defects are removed, it is cut to the required length, centered on the end face of the piercing end of the tube blank, then sent to the heating furnace for heating, and perforated on the piercing machine.