The Ultrasonic flaw detection principle of 15CrMo steel plate

The shipbuilding and offshore platform steel plates are our main products. The shipbuilding and offshore platform steel plates are produced according to ASTM A131/A131M technical standard. Our shipbuilding and offshore platform steel plates accept ABS, LR,CCS, RINA, DNV GL, BV, NK, KR, RMRS and so on classification societies’ inspection and will obtain EN10204 3.2 MTC. The typical shipbuilding 15CrMo steel plate and offshore platform steel grades are grade A/B/D/E, AH32, DH32, EH32, FH32, AH36, DH36, EH36, FH36, AH40, DH40, EH40, FH40, etc.

Our company specializes in the production of steel plates, steel coil, steel sections, welded pipes and seamless pipes products, sales of GB, ASME, ASTM, JIS, DIN, EN, API and other standards and specifications of steel 15CrMo steel plate and deep-processed products, facing the domestic and foreign markets, welcome to call for inquiries. It is a modern high-tech professional enterprise integrating scientific research, production and sales.

S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the 15CrMo steel plate rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of 15CrMo steel plate steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.

"The production method of seamless steel pipe can be roughly divided into cross rolling method (menesmann method) and extrusion method. The cross rolling method (menesmann method) is to pierce the tube blank with the cross roll first, and then extend it with the rolling mill. This method is fast in production, but requires high machinability of tube blank. It is mainly suitable for producing carbon steel and low alloy steel tube, 15CrMo steel plate tube.The extrusion method is to pierce the billet or ingot with a piercer, and then extrude it into a steel tube with an extruder. This method is less efficient than the cross rolling method and is suitable for the production of high-strength alloy steel tubes."

It is very important for a company to have a sound after-sales service system, which better guarantees the interests of customers and increases the reliability of the company's products in the hearts of customers. Our company has a dedicated after-sales service team and good after-sales service reputation, and has been recognized by customers over the past decades. Whenever there is problem about our 15CrMo steel plate steel materials during application on the user site, our after-sales service persons will assist to find solutions at the first time.