high quality S275JR steel plate exporter in UAE

, Wear resistant steel plate is widely used, sometimes it needs to be bent, rolled and cut. Since the wear resistant layer is closely combined with the base plate through metallurgical processing, there is no problem with bending and rolling the wear resistant steel plate under normal conditions. However, if the rolling diameter is less than 300 mm, it will cause problems, so it is not recommended to roll under 300 mm.

Cold formed hot rolled pickled automotive structural steel QSTE500TM
Material QSTE500TM chemical composition (melting analysis)%
Carbon: ≤0.12, Silicon: ≤0.35 ,Manganese: ≤1.70, Phosphorus: ≤0.03, Sulfur: ≤0.025, Titanium: ≤0.22, Niobium: ≤0.09
Aluminum : ≥0.015
Specimen test (tensile, bend, specimen is transverse; Mpa).
Yield strength MPa: ≥500
Tensile strength MPa: 550-700
Elongation: ≥17

We have a professional after-sales service team, the company has developed a clear service process and service standards, after-sales service team members strictly perform after-sales procedures, comply with service standards. The most important thing is that we have set up the correct concept of after-sales service, "customer first, sincere service for users".

Our 1810mm production line successfully rolled 1.2mm × 1250mm ultra-thin specifications high strength automotive steel, and the product quality and performance fully met the standards. In recent years, customers have become increasingly demanding for lightweight vehicles. Our company aims at the market and focuses on the development of thin-gauge high strength automotive S275JR steel plate steel. The research and development personnel adjusted the product composition based on theoretical calculations and drawing on other experiences to meet customers' higher requirements for automotive steel yield strength and tensile strength.